Морфология и термоэлектрические свойства керамики твердых растворов γ-Gd-=SUB=-x-=/SUB=-Dy-=SUB=-1-x-=/SUB=-S-=SUB=-1.5-y-=/SUB=-

Abstract

The temperature dependences of Seebeck coefficient, electrical conductivity (Т=300–873K), thermal conductivity and figure of merit (Т=300–770K) of polycrystalline samples of solid solutions based on gadolinium and dysprosium sulfides with γ-GdxDy1-xS1.49 (x=0.1, 0.2, 0.3, 0.4) composition were studied. It was established that samples morphological features, namely, the specific surface area of crystallites causing a change in the number of deformation centers determines the thermal conductivity of -GdxDy1-xS1.49, and it was found that there is an anomalous decrease in thermal conductivity for composition with х = 0.2. For this composition the lowest values of Seebeck coefficient -371 mkV/K at 873K, electrical resistivity 880 mkΩ∙m at 873K and thermal conductivity 0.68 ± 0.03 W/m·K at 770K were obtained, in this case the thermoelectric figure of merit reaches ZT = 0.23.