Ag Doping Effect on Li[Ni_0.2Li_0.2Mn_0.6]O₂Cathode Material

Abstract

Ag doping effect on $Li[Ni_{0.2}Li_{0.2}Mn_{0.6}]O_2$ cathode material was studied. Specially, we focused on rate performance of Ag doped samples. The $Li[Ni_{0.2}Li_{0.2}Mn_{0.6}]O_2$ powder was prepared by simple combustion method and the Ag was doped using $AgNO_3$ during gelation process. Based on X-ray diffraction analysis, there was no structural change by Ag doping, but the 'metallic' form of Ag was included in the doped powder. Both bare and Ag 1 wt.% doped sample showed similar discharge capacity of 242 mAh/g at 0.2C rate. However, as the increase of charge-discharge rate to 3C, Ag 1 wt.% doped sample showed higher discharge capacity (172 mAh/g) and better cyclic performance than those of bare sample. The discharge capacity of Ag 5 wt.% doped sample was relatively low at all rate condition. However it displayed better rate performance than other samples.