Fabrication of titanium alloy matrix silicon carbide fibre reinforced composite

Abstract

Dilatometric study of the anisotropy of an aluminium alloy sheet obtained by rapid solidification. An Al-1.99%Mn-0.80%Mg-0.60%Cr-0.40%Zr-0.13%Fe-0.05%Ti alloy produced by the twin roller melt spinning technique was characterized in terms of thermal stability at low temperature in the range 80–300K. Differences in thermal expansion coefficients in the three directions were evidenced, and revealed the presence of an anisotropy. The differences are mainly due to the nature of the intermetallic phases present in the aluminium matrix. It is important to note the low thermal expansion coefficient obtained along the direction normal to the rolling plane, as compared to those of aluminium alloys prepared by conventional methods.Cet article présente une étude sur la mesure du coefficient de dilatation thermique α(T) de l'alliage Al-1,99%Mn-0,80%Mg-0,60%Cr-0,40%Zr-0,13%Fe-0.05%Ti, refroidi rapidement par la méthode Twin Roller Melt Spinning, dans l'intervalle de température 80–300K. Les résultats obtenus montrent que α(T) varie d'une direction à une autre: α(T) est alors anisotrope. Cette anisotropie peut être due à la présence des différentes phases intermétalliques dans la matrice. De même, il est intéressant de souligner l'obtention d'un coefficient de dilatation thermique suivant la direction perpendiculaire au plan de laminage relativement faible devant celui des alliages d'aluminium élaborés par les méthodes classiques.