Humidity Controlled Mechanical Properties of Electrospun Polyvinylidene Fluoride (PVDF) Fibers

Abstract

Processing parameters in electrospinning allow us to control the properties of fibers on a molecular level and are able to tailor them for specific applications. In this study, we investigate how relative humidity (RH) affects the mechanical properties of electrospun polyvinylidene fluoride (PVDF). The mechanical properties of single fibers were carried out using a specialized tensile stage. The results from tensile tests were additionally correlated with high-resolution imaging showing the behavior of individual fibers under tensile stress. The mechanical characteristic is strongly dependent on the crystallinity, chain orientation, and fiber diameter of electrospun PVDF fibers. Our results show the importance of controlling RH during electrospinning as the mechanical properties are significantly affected. At low RH = 30% PVDF fibers are 400% stiffer than their counterparts prepared at high RH = 60%. Moreover, the vast differences in the strain at failure were observed, namely 310% compared to 75% for 60% and 30% RH, respectively. Our results prove that humidity is a crucial parameter in electrospinning able to control the mechanical properties of polymer fibers.