Structural, morphological and optical properties of LiCo0.5Ni0.45Ag0.05O2 thin films

Abstract

Pulsed Laser Deposition (PLD) method has been successfully used for the synthesized of nano-crystalline cathode m aterial LiCo0.5Ni0.45Ag0.05O2 (LCNAO) thin film. LCNAO Ferromagnetic using pulsed Nd-YAG laser with wavelength (λ = 532 nm) and duration (10 ns) and energy fluence (1.4 J/cm2) with different substrate temperature (100, 200, 300) ˚C and O2 pressure at 10 mbar. The structural, morphological and optical properties of the films were determined by X-ray Diffraction (XRD), Scan Electron Microscopy (SEM), Atomic Force microscope (AFM) and UV–VIS spectroscopy respectively. It is observed that partial layer to spinel transformation takes place during post annealing and the average particle size of the LiCo0.5Ni0.45Ag0.05O2 is found to be (1-12) nm from SEM measurement. Finally the optical properties of the thin films have been studied at different Substrate temperature. It found the energy gap decreases from 4.2 to 3.8 eV when the substrate's temperature increasing from 100° C into 300 °C of the LCNAO films. These mean that the optical quality of LCNAO films is improved due to the increase in crystalline size and reduction of defect sites.