The Influence of Bi<sub>2</sub>O<sub>3</sub> on SiO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub>-B<sub>2</sub>O<sub>3</sub>-RO Glass Propertiesarts
Ying Liang TianJing ZhangShi Bing SunJi Ye Fan
Abstract
In the paper, regarded SiO 2 -Al 2 O 3 -B 2 O 3 -RO system as basic composition, high-temperature glass glaze was prepared successfully by using Bi 2 O 3 in place of Al 2 O 3 , and traditional melt annealing method was adopted .The influence of Bi 2 O 3 on expansion coefficient, sintering temperature, electrical resistivity was investigated by DIL-2008, SJY sintering imager, Keythley2410. The results show that the sintering temperature of glass glaze has a wide range, which can reach 270°C, so it is easy to sinter; with the increasing of bismuth oxide content, expansion coefficient of glass glaze gradually increases, whereas sintering temperature and electrical resistivity continuously decreases.
Metrics
Citation History
Topics
Related Documents
DETERMINATION OF SiO<SUB>2</SUB>, Al<SUB>2</SUB>O<SUB>3</SUB>, V<SUB>2</SUB>O<SUB>5</SUB> AND Cr<SUB>2</SUB>O<SUB>3</SUB>
Phase Separation of SiO<sub>2</sub>-B<sub>2</sub>O<sub>3</sub>-Al<sub>2</sub>O<sub>3</sub>-ZrO<sub>2</sub>-RO-R<sub>2</sub>O Glasses
On the Compound K<sub>2</sub>O⋅Al<sub>2</sub>O<sub>3</sub>⋅SiO<sub>2</sub> and K<sub>2</sub>O⋅Al<sub>2</sub>O<sub>3</sub>
Permeability of Oxygen through Molten CaO-SiO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub>, Fe<sub>2</sub>O<sub>3</sub>-CaO-SiO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub> and CaF<sub>2</sub>-CaO- SiO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub> Systems
Research on Activities of CaO-SiO<sub>2</sub>-B<sub>2</sub>O<sub>3</sub> (Al<sub>2</sub>O<sub>3</sub>, Fe<sub>2</sub>O<sub>3</sub>) Slag System
Hong Ming WangGui Rong LiXiang ZhuYu Tao Zhao