Distribution of copper-nickel and copper-cobalt between copper-nickel and copper-cobalt alloys and silica saturated fayalite slags

Abstract

AbstractAbstractSolubility experiments have been carried out by equilibrating copper-nickel and copper-cobalt alloys with silica saturated fayalite slags under controlled oxygen pressures (10−6–10−10 atm.) over the temperature range 1250–1350°C. At a constant oxygen pressure and constant temperature, the metal solubility increases with the metal activity in the alloy phase. For a constant metal activity, and constant temperature, the solubility increases with increasing oxygen pressure. Copper is found to depress the solubility of both nickel and cobalt in the slag phase. Increase in temperature is found to decrease the metal solubility. A mechanism based on the oxidation of the metal is postulated. Résumé Des essais de solubilité ont été effectués par l'équilibre des alliages Cu-Ni et Cu-Ca avec des laitiers de fayalite saturés en silice. Ces expériences ont été effectuées dans une fourchette de tempérapture comprise entre 1,250°C et 1,350°C tandis que la pression partielle d'oxygéne était contrôlée (10−6–10−10 atm.).A température et pression d'oxygéne constantes, la solubilite du métal croît avec son activité dans l'alliage. Avec un accroissement de la pression d'oxygene, le métal voit sa solubilité augmentée; l'activité du métal et la température demeurant constantes. Le cuivre diminue la solubilite du nickel et du cobalt dans le laitier. Une augmentation de température produit le même effet. On propose un mécanisme basé sur l'oxydation du métal.