Bioactive surface modification on amide-photografted poly(3-hydroxybutyrate- co -3-hydroxyvalerate)

Abstract

Collagen was chemically immobilized on poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) films via hydrophilic polyacrylamide spacers, aiming to establish the bioactive surface and the inner surface models. The inner surface modified films presented higher wettability than the surface modified films. Wide-angle x-ray diffraction results showed that the d-spacing values of the inner surface model increased compared with those of the surface model, but there was no significant difference between the amide- and collagen-modified PHBV films. The peak melting temperatures of PHBV and the special endotherm around 70 °C were following the order: PHBV > amide-modified PHBV > collagen-modified PHBV. The weight loss of the collagen-modified PHBV (inner surface model) might involve hydrolyzation and mineralization during 360 days of incubation, with a maximum value of 18.24%, while PHBV films did not show significant weight loss. The pH value of the degradation fluids fluctuated in the range of 6.86-7.22, as the initial pH was recorded at 7.20. Based on the surface model, collagen-modified PHBV scaffolds were prepared, which enhanced chondrocyte adhesion and spread on the biomimetic surface. Two surface modification models might develop a protocol with a view to generating a biocompatible and biomechanical scaffold for use in meniscus regeneration.