Preparation and Properties of Organosilicon-Modified Epoxy Esters Resin

Abstract

Organosilicon-modified epoxy esters resin was successfully prepared by solution polymerization and the effect of content of silica sol and silane coupling agent (KH560) on the resistance to water, acid, alkali and film dry, the polymerization mechanism, structure were studied, respectively. The results showed that: compared with the properties of resistance to water, acid, alkali and film dry of pure epoxy esters resin, to some extent, those of organosilicon-modified epoxy esters resin had been improved a lot. The properties of resistance to water, acid, alkali and aging increased at first and then changed little with the increase of the content of organosilicon. Especially, the comprehensive performance of composite resin was relatively excellent when the content of silica sol and KH560 was 10%, respectively. Keywords: Organosilicon; epoxy esters resin; silane coupling agent; solution polymerization