Porous maleic anhydride–styrene–divinylbenzene copolymer beads

Abstract

The formation of the porosity and the pore stability in maleic anhydride–styrene–divinylbenzene (MAn–St–DVB) copolymer beads were investigated using the apparent density measurements of the samples dried from methanol (maximum porosity) and from dioxane (stable porosity). The copolymer beads were prepared by the suspension polymerization method in glycerol instead of water as the dispersing medium. A toluene–dioxane (1:1) mixture was used as the diluent at a fixed volume fraction of the organic phase (0.47). Compared to St–DVB copolymers prepared in the presence of nonsolvating diluents, porous MAn–St–DVB copolymers are obtained at relatively low DVB concentration, i.e., at 1–3% DVB. The porosity of the copolymers increases with decreasing MAn concentration in the feed due to the decrease in the copolymer yield. The results of the elemental analyses and titrimetric methods indicate that approximately only half of the MAn units in the copolymer are able to react with amine or with water. A possible rearrangement of the MAn units into the cyclopentanone structures was suggested.